A cylindrical job with diameter of $$200$$ $$mm$$ and height of $$100$$ $$mm$$ is to be cast using modulus method of riser design. Assume that the bottom surface of cylindrical riser does not contribute as cooling surface. If the diameter of the riser is equal to its height, then the height of the riser (in $$mm$$) is

Heat is removed from a molten metal of mass $$2$$ $$kg$$ at a constant rate of $$10$$ $$kW$$ till it is completely solidified. The cooling curve is shown in the figure.

Assuming uniform temperature throughout the volume of the metal during solidification, the latent heat of fusion of the metal (in $$kJ/kg$$) is ______________

Gray cast iron blocks of size $$100\,\,mm \times 50\,\,mm \times 10\,\,mm$$ with a central spherical cavity of diameter $$4$$ mm are sand cast. The shrinkage allowance for the pattern is $$3\% $$. The ratio of the volume of the pattern to volume of the casting is ___________________

A cube and a sphere made of cast iron (each of volume $$1000\,\,c{m^3}$$) were cast under identical conditions. The time taken for solidifying the cube was $$4$$ $$s.$$ The solidification time (in $$s$$) for the sphere is _____________________